Meeting 2018 TMS Annual Meeting & Exhibition
Symposium Fracture: 65 Years after the Weibull Distribution and the Williams Singularity
Presentation Title K-dominance of Atomistic Cracks
Author(s) Ellad B Tadmor
On-Site Speaker (Planned) Ellad B Tadmor
Abstract Scope In linear elastic fracture mecahnics (LEFM), the region of K-dominance is an annulus at the tip of a crack where the LEFM K-field adequately describes the stress state. The annulus is defined by an inner radius of the nonlinear process zone and an outer radius where higher-order terms in the elastic stress field solution become important. We explore the region of K-dominance for atomistic cracks with stress fields obtained using the MDStressLab package (http://mdstresslab.org/). We explore the crack tip singularity and identify the conditions under which LEFM is applicable in atomic-scale fracture.
Proceedings Inclusion? Planned: Supplemental Proceedings volume

OTHER PAPERS PLANNED FOR THIS SYMPOSIUM

A Data-driven Approach to Predict Microstructurally Small Crack Evolution
A Probability Model for Stress Rupture Failure of Carbon Composites, Incorporating Weibull Fiber Strength Statistics, Local Fiber Load Sharing, and Matrix Creep
An Integrity Basis of Fracture Challenges
Applicability of Weibull Statistics for Micro- and Nano-scale Silicon Components
Comparison of Methods to Find the Weibull Stress Parameters
Composite Overwrapped Pressure Vessel (COPV) Life Test
Computational Procedure for Designing New Gen 3 Steels with High Formability and Ductile Fracture Resistance
E-42: High Temperature Cracking Damage of Calcium Aluminate Cements
E-43: On the Experimental Evaluation of the Fracture Toughness of Shape Memory Alloys
Forward Propagation of Random Microstructural Features for Reliability Estimates of Engineering Structures
Fracture Behavior of High Performance Sheet Steel
Fracture Toughness of Silicon by Variable Temperature Micropillar Splitting
Grain and Sub-grain Level Strains ahead of an Evolving Fatigue Short Crack as Measured by X-ray Techniques
K-dominance of Atomistic Cracks
Limitations and Applicability of LEFM to Spalling Fracture in Single Crystal Semiconductors
NASA's Plan for Development and Transition of Computational Materials-based Capabilities for Next-generation Durability / Damage Tolerance and Additive Manufacturing
On the Prediction of Failure in 6016 Aluminum Alloy Sheet by GISSMO Damage Model
Physical and Computational Aspects of Engineering Damage Mechanics
Predicting Joint Strength: Evaluating Interface Corner Stress Intensity Factor and Cohesive Zone Modeling Approaches
Re-tooling the Engineering Predictive Practices for Durability and Damage Tolerance
Singularities of Dynamic Cracks
Size, Temperature, Environmental Effects on Brittle Fracture (BDT)
The Complexity of Ductile Fracture
The Effect of Loading Rate on Fracture Toughness of Low Ductility Materials
Toughness, Roughness and Crack Path Engineering for Improved Ductile Fracture Resistance
Trends in Microstructure-sensitive Computational Approaches to Fatigue Cracking
Use of Weibull Distribution to Characterize High Performance Fibers
Using R-curves to Predict Fatigue Behavior in Crack Bridging Toughened Ceramics
Void Initiation during Ductile Rupture of Pure Metals
Weibull Analysis of High Strength Ni- and Fe-based Bulk Metallic Glasses

Questions about ProgramMaster? Contact programming@programmaster.org